Quick Details

• Place of Origin: Fujian, China (Mainland)

• Brand Name: Yuxiang

• Model Number: YX-171H

Packaging & Delivery

Packaging Details:	25kg/ bag or customised packing
Delivery Detail:	Within 15 days

Specifications

Polypropylene:
Widely used in plastic field, particularly in fiber and filament
Moderate shock resistance

Product Name: Polypropylene Virgin PP Granules PP Raw Material

Introduction:

Polypropylene, as thermoplastic polymer, is widely used in plastic field. Due to different catalyst and polymerization process, the polymers we gain are different in property and application. PP has many useful properties, but lack of inherent toughness, especially when it below its glass transition temperature, however, by means of adding impact modifier, can enhance its shock resistance.

It is widely used in thermoplastic plastics field, particularly in fiber and filament, thin film extrusion, injection molding process and etc. Main commercial use of the PP of shock resistance is injection molding in automobile, house ware and utensil. Its shock resistance, low density, tinting strength and process ability enables it to be ideal material. Moderate shock resistance, resin grade with higher melt flow velocity has higher flowing property, which can be useful in injection molding larger component, such as panels of automobile.

Application:

Diaper, Car interior Parts, packaging, seedbed cover

Major Characteristics:

1. High flow. narrow molecular weight distribution, controlled rheology grade

2. Suitable for processing of spunbond

Propertles	Test Mathod	Unlt	SFR-171H
Melt Flow Rate at 230C Density Tensile Strength at Yield Elongard On at Break Flexural Modulus Rockwell Hardness IZOD Impact Strength at 23C VICAT Softening Point Heat Distortion Temp	ASTM D 1238 ASTM D 792 ASTM D 638 ASTM D 638 ASTM D 790 ASTM D 785 ASTM D 265 ASTM D 1525 ASTMD 648	g/ 10min g/ cm kg/ cm % Kg/ cm R Kg.cm/ cm C C	34 0.90 350 ) 500 15000 105 2.0 152 109

Physical Property:

The figures indicated on the table are standard vahies.

Processing Condltions

1. Processing temperature : 200-250c

2. Quenching temperature : 10-30c

Correlation of spinning condltions and typical propertles

Increesing of	Shrinkage rae (%)	Elongetion (%)	Tenacity
Draw speed (m/ min)	↑	↓	↑
Draw ratio	↑	↓	↑
Draw temp (c)	↑	-	↓

Typical Physical Property Data: