Resistant to high temperature paint

This series of high-temperature paint is solvent-based paint, has excellent weather and temperature resistance, good adhesion to the substrate strength and abrasion resistance, for a variety of requirements nonstick frying plates, and other kitchen utensils baking sheet resistance coated high temperature and abrasion-resistant coating.

Resin Type: mainly polyester modified silicone resin.

Toxicity: heavy metal content and comply with ASTM F963-96a EN71: Part3: 1994 standards.

Operating temperature: 250 ℃ (long-term)

Paint Specifications:

project
Instrument / Test Method
standard

1. attachment force
10 * 10 hundred grid test, 3M tape
100% does not fall off (after the film hard work and testing before cooling)

2. Resistance to acid
5% acetic acid, soak 24H
Non-foaming

3. Alkali
5% sodium bicarbonate solution, soak 24H
Non-foaming

4. Hardness
Hardness tester, Mitsubishi Pencil
H above

5. abrasion
500g force E-350 eraser rub back and forth
2000 times do not show the bottom

6. resistance to salt fog
5% sodium chloride solution was continuously sprayed 120 hours
Non-foaming

7. solvent resistance
With cotton dipped more than 99 percent of the ethanol rubbing back and forth 50 times
Do not fade

8. resistant to high temperature
250 ℃ continuous bake 24 hours after doing hundred grid test
100% No loss

Construction Description:

1. Surface treatment: steel roughened (80 # sand), phosphate, aluminum and aluminum alloy roughened (80 # sand) oxide

2. Spray Thinner: S-901

3. Spraying viscosity: 10 seconds or more

The optimum thickness: 25 ± 5μm

5. Drying conditions: 80 ℃ ~ 120 ℃ / 10 ~ 15 minutes after 270 ℃ ~ 290 ℃ / 20-15 min

Stir before 6. Using a uniform 30 to 40 rev / min, roll half an hour.

7. Before using 160-180 mesh weave dimensional mesh filter.

Storage conditions: 1. 25 ℃ (sealed) the following storage.

2. Scroll once every two weeks, 30-40 rev / min.

Shelf life: If undiluted retention period of 6 months / 25 ℃ (sealed), after dilution use within a day (if more than storage period, according to project specifications prescribed in this test, if they meet the technical requirements, can still be used).